Spherical CHRONITAL is used in all applications where ferrous residue is a disadvantage or undesired.
CHRONITAL distinguishes itself by having a high percentage of spherical and dense grains.
Its high durability and high energy transfer are convincing, exactly as its low equipment wear characteristic.
All are pre-conditions for a cost effective and stabile blasting process.

By switching to CHRONITAL, users of glass beads are able to reduce their consumption and waste to 1 %.
Dust development during blasting is correspondingly reduced by a large amount. Surface cleanliness,
as well as the entire work conditions are clearly improved.

CHRONITAL is suitable for use in centrifugal wheel blast machines as well as air blast systems and finds use in
cleaning, deburring, hardening, descaling, roughening and surface improvement of:

  • Aluminum, bronze, brass, zinc and stainless castings
  • Aluminum, brass and stainless forgings
  • Aluminum and stainless profiles
  • Stainless wire
  • Stainless and steel components
  • Titanium or nickel-based alloys
  • Concrete paver and natural stone

Areas of Application CHRONITAL

Technical Data

Chemical Composition: C < 0,17%, Cr 18 - 19%, Ni ~ 10%, Si < 3,0%, Mn < 2,0%
Microstructure: Austenitic
Hardness: As produced  ~ 275 HV (28 HRC)
  Operating mix  ~ 475 HV (48 HRC)
Apparant density: ~ 4,7 g/cm3
   

 

Available Grain sizes

CHRONITAL mm CHRONITAL mm
S 10 0,05 - 0,20 S 60 0,70 - 1,20
S 20 0,09 - 0,32 S100 1,00 - 1,40
S 30 0,14 - 0,50 S 150 1,25 - 1,70
S 40 0,40 - 0,80 S 200 1,40 - 2,00
S 50 0,60 - 1,00 S 300 1,70 - 3,00

 Special screenings available upon request. Contact us.

Packing Options

25 kg plastic bag, 500kg per EUR Pallet
500 kg big bag
750 kg metal drum